Spiral (Helix) Teflon Coated

$99.00

 When the exterior surface of a helix shows visible etching, the helix should be discarded.

SKU: PN: CTS214 (2014-SPC) Category:
10 or more pc. discount

Description

The PN:  CTS214 Spirals (Helices) are Teflon coated to be used with our PN:  KSC114 Spiral Contractometer

Specialty Testing spirals are masked on the interior surface with a thin Teflon coating that will withstand repeated stripping of nickel deposits in a 50% nitric acid solution at room temperature. These spirals (helices) will withstand plating bath temperatures up to 300°F.

Specialty Testing and Development Co. spirals (helices) are constructed from 0.010 inch thick stainless steel and
each has a precise surface area of 13.57 square inches. The spiral (helix) mounts on the contractometer in a
manner that permits plating on the entire outside surface of the spiral (helix) and discourages deposition on the
interior of the helix. Thus, there is no need to estimate the surface area that has been plated.

Note: The recommended average test deposit thickness is 500 microinches, (0.000500 inch) for nickel deposits.

PROPERTIES AND TEST CONDITIONS FOR STAINLESS STEEL SPIRAL (HELIX) WITH A TEFLON COATED INTERIOR
Surface Area, in² 13.57
Square Feet 0.0942
Amps per sq. foot 30
Amps 2.90
Stock Thickness, inches 0.010
Avg. Deposit Thickness, µʺ 500
Plating Time, Min & Seconds 20 M & 40 S
Plating Solution Temperature 130°F ± 1 °F.

Equipment Needed:
-Spiral Contractometer with calibration weights (PN:KSC114)
-Adjustable Spiral Contractometer Support Stand (PN: SAS141)
-Titanium anode basket 3.5ʺOD for Wood’s nickel strike (PN:ABS14) * If needed
-Titanium anode basket 5ʺOD for nickel bath (PN:ABL14)
-4,000 ml Pyrex beaker for plating bath (other source)
-DC Power Supply 0-5 Amperage output constant amp constant voltage (PN: HY3005-PS)
-Approx. 3,000 ml beaker for Wood’s nickel strike bath (other source) around 9 1/2” tall beaker *If needed
-Magnetic Stirrer Hot Plate (PN:MSH4000)
-Digital Temperature Controller prewired with probe (PN:590TC)

STRIPPING OF HELIX FOR REUSE.
Plated helices can be stripped of nickel deposits repeatedly in a 50% by volume nitric acid solution for reuse.
Do not heat the solution above 90°F. The Teflon coating remains in place.

*If you have a special request for spiral/ helix please contact the office to see if we can make them per your specifications.

 